N08332 Stainless Steel vs. C63600 Bronze
N08332 stainless steel belongs to the iron alloys classification, while C63600 bronze belongs to the copper alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is N08332 stainless steel and the bottom bar is C63600 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
110 |
Elongation at Break, % | 34 | |
30 to 66 |
Poisson's Ratio | 0.28 | |
0.34 |
Rockwell B Hardness | 77 | |
71 to 84 |
Shear Modulus, GPa | 76 | |
42 |
Shear Strength, MPa | 350 | |
320 to 360 |
Tensile Strength: Ultimate (UTS), MPa | 520 | |
410 to 540 |
Tensile Strength: Yield (Proof), MPa | 210 | |
150 to 260 |
Thermal Properties
Latent Heat of Fusion, J/g | 310 | |
230 |
Maximum Temperature: Mechanical, °C | 1050 | |
210 |
Melting Completion (Liquidus), °C | 1390 | |
1030 |
Melting Onset (Solidus), °C | 1340 | |
980 |
Specific Heat Capacity, J/kg-K | 480 | |
410 |
Thermal Conductivity, W/m-K | 12 | |
57 |
Thermal Expansion, µm/m-K | 16 | |
17 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 1.7 | |
12 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 1.9 | |
13 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 32 | |
30 |
Density, g/cm3 | 8.0 | |
8.6 |
Embodied Carbon, kg CO2/kg material | 5.4 | |
2.8 |
Embodied Energy, MJ/kg | 77 | |
45 |
Embodied Water, L/kg | 190 | |
340 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 | |
98 to 290 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 | |
100 to 300 |
Stiffness to Weight: Axial, points | 14 | |
7.3 |
Stiffness to Weight: Bending, points | 24 | |
19 |
Strength to Weight: Axial, points | 18 | |
13 to 18 |
Strength to Weight: Bending, points | 18 | |
14 to 17 |
Thermal Diffusivity, mm2/s | 3.1 | |
16 |
Thermal Shock Resistance, points | 12 | |
15 to 20 |
Alloy Composition
Aluminum (Al), % | 0 | |
3.0 to 4.0 |
Arsenic (As), % | 0 | |
0 to 0.15 |
Carbon (C), % | 0.050 to 0.1 | |
0 |
Chromium (Cr), % | 17 to 20 | |
0 |
Copper (Cu), % | 0 to 1.0 | |
93 to 96.3 |
Iron (Fe), % | 38.3 to 48.2 | |
0 to 0.15 |
Lead (Pb), % | 0 to 0.0050 | |
0 to 0.050 |
Manganese (Mn), % | 0 to 2.0 | |
0 |
Nickel (Ni), % | 34 to 37 | |
0 to 0.15 |
Phosphorus (P), % | 0 to 0.030 | |
0 |
Silicon (Si), % | 0.75 to 1.5 | |
0.7 to 1.3 |
Sulfur (S), % | 0 to 0.030 | |
0 |
Tin (Sn), % | 0 to 0.025 | |
0 to 0.2 |
Zinc (Zn), % | 0 | |
0 to 0.5 |
Residuals, % | 0 | |
0 to 0.5 |