N08332 Stainless Steel vs. R30155 Cobalt
Both N08332 stainless steel and R30155 cobalt are iron alloys. They have 70% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is N08332 stainless steel and the bottom bar is R30155 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 170 | |
220 |
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
210 |
Elongation at Break, % | 34 | |
34 |
Fatigue Strength, MPa | 170 | |
310 |
Poisson's Ratio | 0.28 | |
0.29 |
Shear Modulus, GPa | 76 | |
81 |
Shear Strength, MPa | 350 | |
570 |
Tensile Strength: Ultimate (UTS), MPa | 520 | |
850 |
Tensile Strength: Yield (Proof), MPa | 210 | |
390 |
Thermal Properties
Latent Heat of Fusion, J/g | 310 | |
300 |
Maximum Temperature: Corrosion, °C | 420 | |
570 |
Maximum Temperature: Mechanical, °C | 1050 | |
1100 |
Melting Completion (Liquidus), °C | 1390 | |
1470 |
Melting Onset (Solidus), °C | 1340 | |
1420 |
Specific Heat Capacity, J/kg-K | 480 | |
450 |
Thermal Conductivity, W/m-K | 12 | |
12 |
Thermal Expansion, µm/m-K | 16 | |
14 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 32 | |
80 |
Density, g/cm3 | 8.0 | |
8.5 |
Embodied Carbon, kg CO2/kg material | 5.4 | |
9.7 |
Embodied Energy, MJ/kg | 77 | |
150 |
Embodied Water, L/kg | 190 | |
300 |
Common Calculations
PREN (Pitting Resistance) | 19 | |
37 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 | |
230 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 | |
370 |
Stiffness to Weight: Axial, points | 14 | |
14 |
Stiffness to Weight: Bending, points | 24 | |
23 |
Strength to Weight: Axial, points | 18 | |
28 |
Strength to Weight: Bending, points | 18 | |
24 |
Thermal Diffusivity, mm2/s | 3.1 | |
3.2 |
Thermal Shock Resistance, points | 12 | |
21 |
Alloy Composition
Carbon (C), % | 0.050 to 0.1 | |
0.080 to 0.16 |
Chromium (Cr), % | 17 to 20 | |
20 to 22.5 |
Cobalt (Co), % | 0 | |
18.5 to 21 |
Copper (Cu), % | 0 to 1.0 | |
0 |
Iron (Fe), % | 38.3 to 48.2 | |
24.3 to 36.2 |
Lead (Pb), % | 0 to 0.0050 | |
0 |
Manganese (Mn), % | 0 to 2.0 | |
1.0 to 2.0 |
Molybdenum (Mo), % | 0 | |
2.5 to 3.5 |
Nickel (Ni), % | 34 to 37 | |
19 to 21 |
Niobium (Nb), % | 0 | |
0.75 to 1.3 |
Nitrogen (N), % | 0 | |
0 to 0.2 |
Phosphorus (P), % | 0 to 0.030 | |
0 to 0.040 |
Silicon (Si), % | 0.75 to 1.5 | |
0 to 1.0 |
Sulfur (S), % | 0 to 0.030 | |
0 to 0.030 |
Tantalum (Ta), % | 0 | |
0.75 to 1.3 |
Tin (Sn), % | 0 to 0.025 | |
0 |
Tungsten (W), % | 0 | |
2.0 to 3.0 |