N08367 Stainless Steel vs. SAE-AISI 1044 Steel

Both N08367 stainless steel and SAE-AISI 1044 steel are iron alloys. They have 46% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is N08367 stainless steel and the bottom bar is SAE-AISI 1044 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
180
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 34
18
Fatigue Strength, MPa 280
230
Poisson's Ratio 0.28
0.29
Reduction in Area, % 56
46
Shear Modulus, GPa 80
72
Shear Strength, MPa 490
380
Tensile Strength: Ultimate (UTS), MPa 740
620
Tensile Strength: Yield (Proof), MPa 350
340

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 12
51
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.8
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.0
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 33
1.8
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.2
1.4
Embodied Energy, MJ/kg 84
18
Embodied Water, L/kg 200
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
94
Resilience: Unit (Modulus of Resilience), kJ/m3 290
320
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25
22
Strength to Weight: Bending, points 22
21
Thermal Diffusivity, mm2/s 3.2
14
Thermal Shock Resistance, points 17
20

Alloy Composition

Carbon (C), % 0 to 0.030
0.43 to 0.5
Chromium (Cr), % 20 to 22
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 41.4 to 50.3
98.8 to 99.27
Manganese (Mn), % 0 to 2.0
0.3 to 0.6
Molybdenum (Mo), % 6.0 to 7.0
0
Nickel (Ni), % 23.5 to 25.5
0
Nitrogen (N), % 0.18 to 0.25
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050