N10629 Nickel vs. SAE-AISI S7 Steel

N10629 nickel belongs to the nickel alloys classification, while SAE-AISI S7 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is N10629 nickel and the bottom bar is SAE-AISI S7 steel.

UNS N10629 Nickel-Molybdenum Alloy SAE-AISI S7 (T41907) Shock-Resisting Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		220
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.31
Poisson's Ratio		0.29

Shear Modulus, GPa		83
Shear Modulus, GPa		74

Tensile Strength: Ultimate (UTS), MPa		860
Tensile Strength: Ultimate (UTS), MPa		670 to 2030

Thermal Properties

Latent Heat of Fusion, J/g		310
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		1610
Melting Completion (Liquidus), °C		1460

Melting Onset (Solidus), °C		1560
Melting Onset (Solidus), °C		1420

Specific Heat Capacity, J/kg-K		390
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		10
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		75
Base Metal Price, % relative		5.0

Density, g/cm³		9.2
Density, g/cm³		7.8

Embodied Carbon, kg CO₂/kg material		15
Embodied Carbon, kg CO₂/kg material		2.3

Embodied Energy, MJ/kg		190
Embodied Energy, MJ/kg		31

Embodied Water, L/kg		270
Embodied Water, L/kg		65

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		22
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		26
Strength to Weight: Axial, points		24 to 72

Strength to Weight: Bending, points		22
Strength to Weight: Bending, points		22 to 46

Thermal Shock Resistance, points		27
Thermal Shock Resistance, points		22 to 66

Alloy Composition

Aluminum (Al), %		0.1 to 0.5
Aluminum (Al), %		0

Carbon (C), %		0 to 0.010
Carbon (C), %		0.45 to 0.55

Chromium (Cr), %		0.5 to 1.5
Chromium (Cr), %		3.0 to 3.5

Cobalt (Co), %		0 to 2.5
Cobalt (Co), %		0

Copper (Cu), %		0 to 0.5
Copper (Cu), %		0 to 0.25

Iron (Fe), %		1.0 to 6.0
Iron (Fe), %		91.6 to 94.9

Manganese (Mn), %		0 to 1.5
Manganese (Mn), %		0.2 to 0.9

Molybdenum (Mo), %		26 to 30
Molybdenum (Mo), %		1.3 to 1.8

Nickel (Ni), %		65 to 72.4
Nickel (Ni), %		0

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 0.050
Silicon (Si), %		0.2 to 1.0

Sulfur (S), %		0 to 0.010
Sulfur (S), %		0 to 0.030

Vanadium (V), %		0
Vanadium (V), %		0 to 0.3