R05240 Alloy vs. AWS BNi-3

R05240 alloy belongs to the otherwise unclassified metals classification, while AWS BNi-3 belongs to the nickel alloys. There are 14 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is R05240 alloy and the bottom bar is AWS BNi-3.

UNS R05240 Tantalum-Niobium Alloy AWS BNi-3 (N99630) Filler Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		150
Elastic (Young's, Tensile) Modulus, GPa		170

Poisson's Ratio		0.36
Poisson's Ratio		0.31

Shear Modulus, GPa		57
Shear Modulus, GPa		66

Tensile Strength: Ultimate (UTS), MPa		270
Tensile Strength: Ultimate (UTS), MPa		430

Thermal Properties

Latent Heat of Fusion, J/g		210
Latent Heat of Fusion, J/g		350

Specific Heat Capacity, J/kg-K		190
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		6.8
Thermal Expansion, µm/m-K		10

Otherwise Unclassified Properties

Density, g/cm³		14
Density, g/cm³		8.3

Embodied Water, L/kg		460
Embodied Water, L/kg		220

Common Calculations

Stiffness to Weight: Axial, points		6.3
Stiffness to Weight: Axial, points		12

Stiffness to Weight: Bending, points		13
Stiffness to Weight: Bending, points		22

Strength to Weight: Axial, points		5.4
Strength to Weight: Axial, points		14

Strength to Weight: Bending, points		6.8
Strength to Weight: Bending, points		15

Thermal Shock Resistance, points		18
Thermal Shock Resistance, points		17

Alloy Composition

Aluminum (Al), %		0
Aluminum (Al), %		0 to 0.050

Boron (B), %		0
Boron (B), %		2.8 to 3.5

Carbon (C), %		0 to 0.010
Carbon (C), %		0 to 0.060

Cobalt (Co), %		0
Cobalt (Co), %		0 to 0.1

Hydrogen (H), %		0 to 0.0015
Hydrogen (H), %		0

Iron (Fe), %		0 to 0.010
Iron (Fe), %		0 to 0.5

Molybdenum (Mo), %		0 to 0.020
Molybdenum (Mo), %		0

Nickel (Ni), %		0 to 0.010
Nickel (Ni), %		90.1 to 93.3

Niobium (Nb), %		35 to 42
Niobium (Nb), %		0

Nitrogen (N), %		0 to 0.010
Nitrogen (N), %		0

Oxygen (O), %		0 to 0.020
Oxygen (O), %		0

Phosphorus (P), %		0
Phosphorus (P), %		0 to 0.020

Selenium (Se), %		0
Selenium (Se), %		0 to 0.0050

Silicon (Si), %		0 to 0.0050
Silicon (Si), %		4.0 to 5.0

Sulfur (S), %		0
Sulfur (S), %		0 to 0.020

Tantalum (Ta), %		57.9 to 65
Tantalum (Ta), %		0

Titanium (Ti), %		0 to 0.010
Titanium (Ti), %		0 to 0.050

Tungsten (W), %		0 to 0.050
Tungsten (W), %		0

Zirconium (Zr), %		0
Zirconium (Zr), %		0 to 0.050

Residuals, %		0
Residuals, %		0 to 0.5