MakeItFrom.com
Menu (ESC)

R05240 Alloy vs. Monel 400

R05240 alloy belongs to the otherwise unclassified metals classification, while Monel 400 belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is R05240 alloy and the bottom bar is Monel 400.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 150
160
Elongation at Break, % 25
20 to 40
Poisson's Ratio 0.36
0.32
Shear Modulus, GPa 57
62
Tensile Strength: Ultimate (UTS), MPa 270
540 to 780
Tensile Strength: Yield (Proof), MPa 170
210 to 590

Thermal Properties

Latent Heat of Fusion, J/g 210
270
Specific Heat Capacity, J/kg-K 190
430
Thermal Expansion, µm/m-K 6.8
14

Otherwise Unclassified Properties

Density, g/cm3 14
8.9
Embodied Water, L/kg 460
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 59
140 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 90
140 to 1080
Stiffness to Weight: Axial, points 6.3
10
Stiffness to Weight: Bending, points 13
21
Strength to Weight: Axial, points 5.4
17 to 25
Strength to Weight: Bending, points 6.8
17 to 21
Thermal Shock Resistance, points 18
17 to 25

Alloy Composition

Carbon (C), % 0 to 0.010
0 to 0.3
Copper (Cu), % 0
28 to 34
Hydrogen (H), % 0 to 0.0015
0
Iron (Fe), % 0 to 0.010
0 to 2.5
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0 to 0.020
0
Nickel (Ni), % 0 to 0.010
63 to 72
Niobium (Nb), % 35 to 42
0
Nitrogen (N), % 0 to 0.010
0
Oxygen (O), % 0 to 0.020
0
Silicon (Si), % 0 to 0.0050
0 to 0.5
Sulfur (S), % 0
0 to 0.024
Tantalum (Ta), % 57.9 to 65
0
Titanium (Ti), % 0 to 0.010
0
Tungsten (W), % 0 to 0.050
0