R05252 Alloy vs. Grade 364 Molybdenum
Both R05252 alloy and grade 364 molybdenum are otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is R05252 alloy and the bottom bar is grade 364 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 310 |
| Elongation at Break, % | 23 | |
| 6.2 to 11 |
| Poisson's Ratio | 0.33 | |
| 0.31 |
| Shear Modulus, GPa | 73 | |
| 120 |
| Tensile Strength: Ultimate (UTS), MPa | 310 | |
| 580 to 720 |
| Tensile Strength: Yield (Proof), MPa | 220 | |
| 350 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 140 | |
| 370 |
| Specific Heat Capacity, J/kg-K | 140 | |
| 250 |
| Thermal Expansion, µm/m-K | 6.7 | |
| 7.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 17 | |
| 10 |
| Embodied Water, L/kg | 600 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 63 | |
| 43 to 57 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 | |
| 200 to 630 |
| Stiffness to Weight: Axial, points | 6.5 | |
| 17 |
| Stiffness to Weight: Bending, points | 12 | |
| 22 |
| Strength to Weight: Axial, points | 5.2 | |
| 16 to 20 |
| Strength to Weight: Bending, points | 6.1 | |
| 15 to 17 |
| Thermal Shock Resistance, points | 17 | |
| 19 to 24 |
Alloy Composition
| Carbon (C), % | 0 to 0.010 | |
| 0.010 to 0.040 |
| Hydrogen (H), % | 0 to 0.0015 | |
| 0 |
| Iron (Fe), % | 0 to 0.010 | |
| 0 to 0.010 |
| Molybdenum (Mo), % | 0 to 0.020 | |
| 99.2 to 99.5 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 to 0.0050 |
| Niobium (Nb), % | 0 to 0.1 | |
| 0 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 to 0.0020 |
| Oxygen (O), % | 0 to 0.015 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Tantalum (Ta), % | 88.8 to 91 | |
| 0 |
| Titanium (Ti), % | 0 to 0.010 | |
| 0.4 to 0.55 |
| Tungsten (W), % | 9.0 to 11 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0.060 to 0.12 |