R30605 Cobalt vs. ASTM A217 Cast Steel
R30605 cobalt belongs to the cobalt alloys classification, while ASTM A217 cast steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is R30605 cobalt and the bottom bar is ASTM A217 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 34 | |
| 21 to 27 |
| Fatigue Strength, MPa | 260 to 590 | |
| 200 to 320 |
| Poisson's Ratio | 0.29 | |
| 0.28 to 0.29 |
| Shear Modulus, GPa | 81 | |
| 73 to 75 |
| Tensile Strength: Ultimate (UTS), MPa | 1130 to 1900 | |
| 540 to 710 |
| Tensile Strength: Yield (Proof), MPa | 470 to 1600 | |
| 270 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 to 270 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1450 to 1460 |
| Melting Onset (Solidus), °C | 1330 | |
| 1410 to 1420 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 470 |
| Thermal Conductivity, W/m-K | 9.6 | |
| 26 to 50 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 7.3 to 9.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.8 | |
| 8.4 to 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 9.8 | |
| 1.5 to 2.1 |
| Embodied Energy, MJ/kg | 140 | |
| 20 to 28 |
| Embodied Water, L/kg | 450 | |
| 47 to 87 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 13 to 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 to 25 |
| Strength to Weight: Axial, points | 33 to 55 | |
| 19 to 25 |
| Strength to Weight: Bending, points | 25 to 36 | |
| 19 to 23 |
| Thermal Diffusivity, mm2/s | 2.5 | |
| 6.9 to 14 |
| Thermal Shock Resistance, points | 31 to 52 | |
| 16 to 20 |