R30605 Cobalt vs. Austempered Cast Iron

R30605 cobalt belongs to the cobalt alloys classification, while austempered cast iron belongs to the iron alloys. There are 22 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is R30605 cobalt and the bottom bar is austempered cast iron.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
180
Elongation at Break, % 34
1.1 to 13
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 81
62 to 69
Tensile Strength: Ultimate (UTS), MPa 1130 to 1900
860 to 1800
Tensile Strength: Yield (Proof), MPa 470 to 1600
560 to 1460

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Melting Completion (Liquidus), °C 1410
1380
Melting Onset (Solidus), °C 1330
1340
Specific Heat Capacity, J/kg-K 410
490
Thermal Conductivity, W/m-K 9.6
42
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Density, g/cm3 9.6
7.5
Embodied Carbon, kg CO2/kg material 9.8
1.8
Embodied Energy, MJ/kg 140
25
Embodied Water, L/kg 450
48

Common Calculations

Stiffness to Weight: Axial, points 12
13
Stiffness to Weight: Bending, points 21
25
Strength to Weight: Axial, points 33 to 55
32 to 66
Strength to Weight: Bending, points 25 to 36
27 to 44
Thermal Diffusivity, mm2/s 2.5
11
Thermal Shock Resistance, points 31 to 52
25 to 53

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Arsenic (As), % 0
0 to 0.020
Carbon (C), % 0.050 to 0.15
3.4 to 3.8
Chromium (Cr), % 19 to 21
0 to 0.1
Cobalt (Co), % 46.4 to 57
0
Copper (Cu), % 0
0 to 0.8
Iron (Fe), % 0 to 3.0
89.6 to 94
Magnesium (Mg), % 0
0 to 0.040
Manganese (Mn), % 1.0 to 2.0
0.3 to 0.4
Molybdenum (Mo), % 0
0 to 0.3
Nickel (Ni), % 9.0 to 11
0 to 2.0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Selenium (Se), % 0
0 to 0.030
Silicon (Si), % 0 to 0.4
2.3 to 2.7
Sulfur (S), % 0 to 0.030
0 to 0.020
Tin (Sn), % 0
0 to 0.020
Tungsten (W), % 14 to 16
0
Vanadium (V), % 0
0 to 0.1