R30605 Cobalt vs. EN 1.5525 Steel
R30605 cobalt belongs to the cobalt alloys classification, while EN 1.5525 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is R30605 cobalt and the bottom bar is EN 1.5525 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 34 | |
| 11 to 21 |
| Fatigue Strength, MPa | 260 to 590 | |
| 210 to 310 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 81 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 1130 to 1900 | |
| 440 to 1440 |
| Tensile Strength: Yield (Proof), MPa | 470 to 1600 | |
| 300 to 490 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1460 |
| Melting Onset (Solidus), °C | 1330 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 470 |
| Thermal Conductivity, W/m-K | 9.6 | |
| 50 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.8 | |
| 8.2 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 9.8 | |
| 1.4 |
| Embodied Energy, MJ/kg | 140 | |
| 19 |
| Embodied Water, L/kg | 450 | |
| 48 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 33 to 55 | |
| 16 to 51 |
| Strength to Weight: Bending, points | 25 to 36 | |
| 16 to 36 |
| Thermal Diffusivity, mm2/s | 2.5 | |
| 13 |
| Thermal Shock Resistance, points | 31 to 52 | |
| 13 to 42 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0.050 to 0.15 | |
| 0.18 to 0.23 |
| Chromium (Cr), % | 19 to 21 | |
| 0 to 0.3 |
| Cobalt (Co), % | 46.4 to 57 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 3.0 | |
| 97.7 to 98.9 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0.9 to 1.2 |
| Nickel (Ni), % | 9.0 to 11 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |
| Tungsten (W), % | 14 to 16 | |
| 0 |