R30816 Cobalt vs. SAE-AISI P2 Steel
R30816 cobalt belongs to the cobalt alloys classification, while SAE-AISI P2 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is R30816 cobalt and the bottom bar is SAE-AISI P2 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Poisson's Ratio | 0.3 | |
| 0.29 |
| Shear Modulus, GPa | 81 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 1020 | |
| 330 to 1980 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Melting Completion (Liquidus), °C | 1540 | |
| 1460 |
| Melting Onset (Solidus), °C | 1460 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 46 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.1 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 20 | |
| 1.5 |
| Embodied Energy, MJ/kg | 320 | |
| 20 |
| Embodied Water, L/kg | 440 | |
| 51 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 22 | |
| 24 |
| Strength to Weight: Axial, points | 31 | |
| 12 to 70 |
| Strength to Weight: Bending, points | 25 | |
| 14 to 45 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 12 |
| Thermal Shock Resistance, points | 28 | |
| 11 to 65 |
Alloy Composition
| Carbon (C), % | 0.32 to 0.42 | |
| 0 to 0.1 |
| Chromium (Cr), % | 19 to 21 | |
| 0.75 to 1.3 |
| Cobalt (Co), % | 40 to 49.8 | |
| 0 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 0 to 5.0 | |
| 96.6 to 98.8 |
| Manganese (Mn), % | 1.0 to 2.0 | |
| 0.1 to 0.4 |
| Molybdenum (Mo), % | 3.5 to 4.5 | |
| 0.15 to 0.4 |
| Nickel (Ni), % | 19 to 21 | |
| 0.1 to 0.5 |
| Niobium (Nb), % | 3.5 to 4.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.1 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 3.5 to 4.5 | |
| 0 |
| Tungsten (W), % | 3.5 to 4.5 | |
| 0 |