R60706 Alloy vs. EN 1.0314 Steel

R60706 alloy belongs to the otherwise unclassified metals classification, while EN 1.0314 steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is R60706 alloy and the bottom bar is EN 1.0314 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 98
190
Elongation at Break, % 16
24 to 25
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 37
73
Tensile Strength: Ultimate (UTS), MPa 580
320 to 400
Tensile Strength: Yield (Proof), MPa 390
190 to 310

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Specific Heat Capacity, J/kg-K 270
470
Thermal Conductivity, W/m-K 17
53
Thermal Expansion, µm/m-K 6.3
12

Otherwise Unclassified Properties

Density, g/cm3 6.7
7.9
Embodied Water, L/kg 450
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 82
68 to 87
Resilience: Unit (Modulus of Resilience), kJ/m3 760
95 to 250
Stiffness to Weight: Axial, points 8.1
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 24
11 to 14
Strength to Weight: Bending, points 23
13 to 15
Thermal Diffusivity, mm2/s 9.5
14
Thermal Shock Resistance, points 67
10 to 13

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.050
0 to 0.030
Chromium (Cr), % 0 to 0.2
0
Hafnium (Hf), % 0 to 4.5
0
Hydrogen (H), % 0 to 0.0050
0
Iron (Fe), % 0 to 0.2
99.365 to 99.78
Manganese (Mn), % 0
0.2 to 0.4
Niobium (Nb), % 2.0 to 3.0
0
Nitrogen (N), % 0 to 0.025
0
Oxygen (O), % 0 to 0.16
0
Phosphorus (P), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.1
Sulfur (S), % 0
0 to 0.025
Zirconium (Zr), % 91 to 98
0