S15700 Stainless Steel vs. ASTM A182 Grade F5a
Both S15700 stainless steel and ASTM A182 grade F5a are iron alloys. They have 80% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is S15700 stainless steel and the bottom bar is ASTM A182 grade F5a.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 460 | |
| 310 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 1.1 to 29 | |
| 25 |
| Fatigue Strength, MPa | 370 to 770 | |
| 380 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 74 |
| Shear Strength, MPa | 770 to 1070 | |
| 450 |
| Tensile Strength: Ultimate (UTS), MPa | 1180 to 1890 | |
| 710 |
| Tensile Strength: Yield (Proof), MPa | 500 to 1770 | |
| 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 870 | |
| 510 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 16 | |
| 40 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 8.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 9.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 4.5 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 1.8 |
| Embodied Energy, MJ/kg | 47 | |
| 24 |
| Embodied Water, L/kg | 140 | |
| 69 |
Common Calculations
| PREN (Pitting Resistance) | 23 | |
| 6.8 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 17 to 270 | |
| 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 640 to 4660 | |
| 700 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 42 to 67 | |
| 25 |
| Strength to Weight: Bending, points | 32 to 43 | |
| 23 |
| Thermal Diffusivity, mm2/s | 4.2 | |
| 11 |
| Thermal Shock Resistance, points | 39 to 63 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0.75 to 1.5 | |
| 0 |
| Carbon (C), % | 0 to 0.090 | |
| 0 to 0.25 |
| Chromium (Cr), % | 14 to 16 | |
| 4.0 to 6.0 |
| Iron (Fe), % | 69.6 to 76.8 | |
| 91.4 to 95.6 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 0.6 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0.44 to 0.65 |
| Nickel (Ni), % | 6.5 to 7.7 | |
| 0 to 0.5 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |