S15700 Stainless Steel vs. EN 1.7240 Steel
Both S15700 stainless steel and EN 1.7240 steel are iron alloys. They have 75% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is S15700 stainless steel and the bottom bar is EN 1.7240 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 460 | |
| 200 to 480 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 1180 to 1890 | |
| 670 to 1990 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 870 | |
| 420 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 16 | |
| 44 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.3 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 2.4 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 47 | |
| 20 |
| Embodied Water, L/kg | 140 | |
| 50 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 42 to 67 | |
| 24 to 71 |
| Strength to Weight: Bending, points | 32 to 43 | |
| 22 to 45 |
| Thermal Diffusivity, mm2/s | 4.2 | |
| 12 |
| Thermal Shock Resistance, points | 39 to 63 | |
| 20 to 59 |
Alloy Composition
| Aluminum (Al), % | 0.75 to 1.5 | |
| 0 |
| Carbon (C), % | 0 to 0.090 | |
| 0.56 to 0.64 |
| Chromium (Cr), % | 14 to 16 | |
| 0.7 to 1.0 |
| Iron (Fe), % | 69.6 to 76.8 | |
| 96.7 to 97.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.7 to 1.0 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0.15 to 0.25 |
| Nickel (Ni), % | 6.5 to 7.7 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |