S21600 Stainless Steel vs. CC497K Bronze

S21600 stainless steel belongs to the iron alloys classification, while CC497K bronze belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is S21600 stainless steel and the bottom bar is CC497K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
55
Elastic (Young's, Tensile) Modulus, GPa 200
93
Elongation at Break, % 46
6.7
Poisson's Ratio 0.28
0.36
Shear Modulus, GPa 79
34
Tensile Strength: Ultimate (UTS), MPa 710
190
Tensile Strength: Yield (Proof), MPa 390
91

Thermal Properties

Latent Heat of Fusion, J/g 290
160
Maximum Temperature: Mechanical, °C 990
130
Melting Completion (Liquidus), °C 1420
870
Melting Onset (Solidus), °C 1380
800
Specific Heat Capacity, J/kg-K 480
330
Thermal Expansion, µm/m-K 17
20

Otherwise Unclassified Properties

Base Metal Price, % relative 17
29
Density, g/cm3 7.7
9.3
Embodied Carbon, kg CO2/kg material 3.6
3.0
Embodied Energy, MJ/kg 50
48
Embodied Water, L/kg 160
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 270
10
Resilience: Unit (Modulus of Resilience), kJ/m3 370
45
Stiffness to Weight: Axial, points 14
5.5
Stiffness to Weight: Bending, points 25
16
Strength to Weight: Axial, points 25
5.6
Strength to Weight: Bending, points 23
7.8
Thermal Shock Resistance, points 15
7.2

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.75
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17.5 to 22
0
Copper (Cu), % 0
67.5 to 77.5
Iron (Fe), % 57.6 to 67.8
0 to 0.25
Lead (Pb), % 0
18 to 23
Manganese (Mn), % 7.5 to 9.0
0 to 0.2
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 5.0 to 7.0
0.5 to 2.5
Nitrogen (N), % 0.25 to 0.5
0
Phosphorus (P), % 0 to 0.045
0 to 0.1
Silicon (Si), % 0 to 0.75
0 to 0.010
Sulfur (S), % 0 to 0.030
0 to 0.1
Tin (Sn), % 0
4.0 to 6.0
Zinc (Zn), % 0
0 to 2.0