S21600 Stainless Steel vs. C14500 Copper
S21600 stainless steel belongs to the iron alloys classification, while C14500 copper belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is S21600 stainless steel and the bottom bar is C14500 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 120 |
| Elongation at Break, % | 46 | |
| 12 to 50 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 79 | |
| 43 |
| Shear Strength, MPa | 500 | |
| 150 to 190 |
| Tensile Strength: Ultimate (UTS), MPa | 710 | |
| 220 to 330 |
| Tensile Strength: Yield (Proof), MPa | 390 | |
| 69 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 990 | |
| 200 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1080 |
| Melting Onset (Solidus), °C | 1380 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 390 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 17 | |
| 33 |
| Density, g/cm3 | 7.7 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 2.6 |
| Embodied Energy, MJ/kg | 50 | |
| 42 |
| Embodied Water, L/kg | 160 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 270 | |
| 36 to 85 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 370 | |
| 21 to 300 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 25 | |
| 6.8 to 10 |
| Strength to Weight: Bending, points | 23 | |
| 9.1 to 12 |
| Thermal Shock Resistance, points | 15 | |
| 8.0 to 12 |
Alloy Composition
| Carbon (C), % | 0 to 0.080 | |
| 0 |
| Chromium (Cr), % | 17.5 to 22 | |
| 0 |
| Copper (Cu), % | 0 | |
| 99.2 to 99.596 |
| Iron (Fe), % | 57.6 to 67.8 | |
| 0 |
| Manganese (Mn), % | 7.5 to 9.0 | |
| 0 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 0 |
| Nickel (Ni), % | 5.0 to 7.0 | |
| 0 |
| Nitrogen (N), % | 0.25 to 0.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0.0040 to 0.012 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tellurium (Te), % | 0 | |
| 0.4 to 0.7 |