S32654 Stainless Steel vs. EN 1.0481 Steel

Both S32654 stainless steel and EN 1.0481 steel are iron alloys. They have 44% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is S32654 stainless steel and the bottom bar is EN 1.0481 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
150
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 45
24
Fatigue Strength, MPa 450
210
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 82
73
Shear Strength, MPa 590
330
Tensile Strength: Ultimate (UTS), MPa 850
510
Tensile Strength: Yield (Proof), MPa 490
300

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 11
50
Thermal Expansion, µm/m-K 15
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 34
2.2
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 6.4
1.5
Embodied Energy, MJ/kg 87
20
Embodied Water, L/kg 220
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 330
100
Resilience: Unit (Modulus of Resilience), kJ/m3 570
230
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 29
18
Strength to Weight: Bending, points 25
18
Thermal Diffusivity, mm2/s 2.9
13
Thermal Shock Resistance, points 19
16

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0 to 0.020
0.080 to 0.2
Chromium (Cr), % 24 to 25
0 to 0.3
Copper (Cu), % 0.3 to 0.6
0 to 0.3
Iron (Fe), % 38.3 to 45.3
96.8 to 99
Manganese (Mn), % 2.0 to 4.0
0.9 to 1.5
Molybdenum (Mo), % 7.0 to 8.0
0 to 0.080
Nickel (Ni), % 21 to 23
0 to 0.3
Niobium (Nb), % 0
0 to 0.020
Nitrogen (N), % 0.45 to 0.55
0 to 0.012
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0 to 0.0050
0 to 0.010
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.020