S32750 Stainless Steel vs. EN 1.4596 Stainless Steel

Both S32750 stainless steel and EN 1.4596 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is S32750 stainless steel and the bottom bar is EN 1.4596 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 81
76
Tensile Strength: Ultimate (UTS), MPa 860
1030 to 1600

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
450
Maximum Temperature: Mechanical, °C 1100
790
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 12
11

Otherwise Unclassified Properties

Base Metal Price, % relative 21
15
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.1
3.5
Embodied Energy, MJ/kg 56
48
Embodied Water, L/kg 180
130

Common Calculations

PREN (Pitting Resistance) 43
19
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 31
36 to 56
Strength to Weight: Bending, points 26
29 to 39
Thermal Shock Resistance, points 25
35 to 54

Alloy Composition

Aluminum (Al), % 0
0.8 to 1.1
Carbon (C), % 0 to 0.030
0 to 0.015
Chromium (Cr), % 24 to 26
11.5 to 12.5
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 58.1 to 66.8
73.4 to 76.4
Manganese (Mn), % 0 to 1.2
0 to 0.1
Molybdenum (Mo), % 3.0 to 5.0
1.9 to 2.2
Nickel (Ni), % 6.0 to 8.0
9.2 to 10.2
Nitrogen (N), % 0.24 to 0.32
0 to 0.020
Phosphorus (P), % 0 to 0.035
0 to 0.010
Silicon (Si), % 0 to 0.8
0 to 0.1
Sulfur (S), % 0 to 0.020
0 to 0.0050
Titanium (Ti), % 0
0.28 to 0.4