S44735 Stainless Steel vs. AISI 416 Stainless Steel
Both S44735 stainless steel and AISI 416 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is S44735 stainless steel and the bottom bar is AISI 416 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 220 | |
| 230 to 320 |
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 21 | |
| 13 to 31 |
| Fatigue Strength, MPa | 300 | |
| 230 to 340 |
| Poisson's Ratio | 0.27 | |
| 0.28 |
| Shear Modulus, GPa | 82 | |
| 76 |
| Shear Strength, MPa | 390 | |
| 340 to 480 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 510 to 800 |
| Tensile Strength: Yield (Proof), MPa | 460 | |
| 290 to 600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 270 |
| Maximum Temperature: Corrosion, °C | 650 | |
| 390 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 680 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1530 |
| Melting Onset (Solidus), °C | 1420 | |
| 1480 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Expansion, µm/m-K | 11 | |
| 9.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 21 | |
| 7.0 |
| Density, g/cm3 | 7.7 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 4.4 | |
| 1.9 |
| Embodied Energy, MJ/kg | 61 | |
| 27 |
| Embodied Water, L/kg | 180 | |
| 100 |
Common Calculations
| PREN (Pitting Resistance) | 42 | |
| 13 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 98 to 140 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 520 | |
| 220 to 940 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 26 | |
| 25 |
| Strength to Weight: Axial, points | 23 | |
| 18 to 29 |
| Strength to Weight: Bending, points | 21 | |
| 18 to 25 |
| Thermal Shock Resistance, points | 20 | |
| 19 to 30 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.15 |
| Chromium (Cr), % | 28 to 30 | |
| 12 to 14 |
| Iron (Fe), % | 60.7 to 68.4 | |
| 83.2 to 87.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.3 |
| Molybdenum (Mo), % | 3.6 to 4.2 | |
| 0 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 |
| Niobium (Nb), % | 0.2 to 1.0 | |
| 0 |
| Nitrogen (N), % | 0 to 0.045 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.060 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0.15 to 0.35 |
| Titanium (Ti), % | 0.2 to 1.0 | |
| 0 |