S46500 Stainless Steel vs. EN 1.4301 Stainless Steel
Both S46500 stainless steel and EN 1.4301 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is S46500 stainless steel and the bottom bar is EN 1.4301 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
200 |
Elongation at Break, % | 2.3 to 14 | |
14 to 46 |
Fatigue Strength, MPa | 550 to 890 | |
200 to 330 |
Poisson's Ratio | 0.28 | |
0.28 |
Shear Modulus, GPa | 75 | |
77 |
Shear Strength, MPa | 730 to 1120 | |
430 to 550 |
Tensile Strength: Ultimate (UTS), MPa | 1260 to 1930 | |
610 to 900 |
Tensile Strength: Yield (Proof), MPa | 1120 to 1810 | |
220 to 570 |
Thermal Properties
Latent Heat of Fusion, J/g | 280 | |
290 |
Maximum Temperature: Corrosion, °C | 680 | |
420 |
Maximum Temperature: Mechanical, °C | 780 | |
940 |
Melting Completion (Liquidus), °C | 1450 | |
1430 |
Melting Onset (Solidus), °C | 1410 | |
1380 |
Specific Heat Capacity, J/kg-K | 470 | |
480 |
Thermal Expansion, µm/m-K | 11 | |
16 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 15 | |
15 |
Density, g/cm3 | 7.9 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 3.6 | |
3.0 |
Embodied Energy, MJ/kg | 51 | |
43 |
Embodied Water, L/kg | 120 | |
140 |
Common Calculations
PREN (Pitting Resistance) | 15 | |
19 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 210 | |
110 to 220 |
Stiffness to Weight: Axial, points | 14 | |
14 |
Stiffness to Weight: Bending, points | 25 | |
25 |
Strength to Weight: Axial, points | 44 to 68 | |
22 to 32 |
Strength to Weight: Bending, points | 33 to 44 | |
20 to 27 |
Thermal Shock Resistance, points | 44 to 67 | |
14 to 20 |
Alloy Composition
Carbon (C), % | 0 to 0.020 | |
0 to 0.070 |
Chromium (Cr), % | 11 to 12.5 | |
17.5 to 19.5 |
Iron (Fe), % | 72.6 to 76.1 | |
66.8 to 74.5 |
Manganese (Mn), % | 0 to 0.25 | |
0 to 2.0 |
Molybdenum (Mo), % | 0.75 to 1.3 | |
0 |
Nickel (Ni), % | 10.7 to 11.3 | |
8.0 to 10.5 |
Nitrogen (N), % | 0 to 0.010 | |
0 to 0.1 |
Phosphorus (P), % | 0 to 0.015 | |
0 to 0.045 |
Silicon (Si), % | 0 to 0.25 | |
0 to 1.0 |
Sulfur (S), % | 0 to 0.010 | |
0 to 0.015 |
Titanium (Ti), % | 1.5 to 1.8 | |
0 |