S46910 Stainless Steel vs. AWS ERTi-12
S46910 stainless steel belongs to the iron alloys classification, while AWS ERTi-12 belongs to the titanium alloys. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is S46910 stainless steel and the bottom bar is AWS ERTi-12.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 110 |
| Elongation at Break, % | 2.2 to 11 | |
| 12 |
| Fatigue Strength, MPa | 250 to 1020 | |
| 200 |
| Poisson's Ratio | 0.28 | |
| 0.32 |
| Shear Modulus, GPa | 76 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 2470 | |
| 480 |
| Tensile Strength: Yield (Proof), MPa | 450 to 2290 | |
| 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 810 | |
| 320 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1670 |
| Melting Onset (Solidus), °C | 1420 | |
| 1620 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 540 |
| Thermal Expansion, µm/m-K | 11 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 18 | |
| 37 |
| Density, g/cm3 | 7.9 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 4.1 | |
| 31 |
| Embodied Energy, MJ/kg | 55 | |
| 510 |
| Embodied Water, L/kg | 140 | |
| 110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 to 130 | |
| 52 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 to 4780 | |
| 550 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 35 |
| Strength to Weight: Axial, points | 24 to 86 | |
| 30 |
| Strength to Weight: Bending, points | 22 to 51 | |
| 30 |
| Thermal Shock Resistance, points | 23 to 84 | |
| 37 |
Alloy Composition
| Aluminum (Al), % | 0.15 to 0.5 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.030 |
| Chromium (Cr), % | 11 to 13 | |
| 0 |
| Copper (Cu), % | 1.5 to 3.5 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0080 |
| Iron (Fe), % | 65 to 76 | |
| 0 to 0.15 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 3.0 to 5.0 | |
| 0.2 to 0.4 |
| Nickel (Ni), % | 8.0 to 10 | |
| 0.060 to 0.090 |
| Nitrogen (N), % | 0 | |
| 0 to 0.015 |
| Oxygen (O), % | 0 | |
| 0.080 to 0.16 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.7 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Titanium (Ti), % | 0.5 to 1.2 | |
| 99.147 to 99.66 |