S46910 Stainless Steel vs. SAE-AISI 1065 Steel
Both S46910 stainless steel and SAE-AISI 1065 steel are iron alloys. They have 71% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is S46910 stainless steel and the bottom bar is SAE-AISI 1065 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 270 to 630 | |
| 210 to 230 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 2.2 to 11 | |
| 11 to 14 |
| Fatigue Strength, MPa | 250 to 1020 | |
| 270 to 340 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 72 |
| Shear Strength, MPa | 410 to 1410 | |
| 430 to 470 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 2470 | |
| 710 to 780 |
| Tensile Strength: Yield (Proof), MPa | 450 to 2290 | |
| 430 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 810 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Expansion, µm/m-K | 11 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 18 | |
| 1.8 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 55 | |
| 19 |
| Embodied Water, L/kg | 140 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 to 130 | |
| 74 to 90 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 to 4780 | |
| 490 to 820 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 24 to 86 | |
| 25 to 28 |
| Strength to Weight: Bending, points | 22 to 51 | |
| 23 to 24 |
| Thermal Shock Resistance, points | 23 to 84 | |
| 25 to 27 |
Alloy Composition
| Aluminum (Al), % | 0.15 to 0.5 | |
| 0 |
| Carbon (C), % | 0 to 0.030 | |
| 0.6 to 0.7 |
| Chromium (Cr), % | 11 to 13 | |
| 0 |
| Copper (Cu), % | 1.5 to 3.5 | |
| 0 |
| Iron (Fe), % | 65 to 76 | |
| 98.3 to 98.8 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 3.0 to 5.0 | |
| 0 |
| Nickel (Ni), % | 8.0 to 10 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.7 | |
| 0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.050 |
| Titanium (Ti), % | 0.5 to 1.2 | |
| 0 |