S46910 Stainless Steel vs. ZA-8
S46910 stainless steel belongs to the iron alloys classification, while ZA-8 belongs to the zinc alloys. There are 27 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is S46910 stainless steel and the bottom bar is ZA-8.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 270 to 630 | |
| 87 to 100 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 85 to 86 |
| Elongation at Break, % | 2.2 to 11 | |
| 1.3 to 8.0 |
| Fatigue Strength, MPa | 250 to 1020 | |
| 51 to 100 |
| Poisson's Ratio | 0.28 | |
| 0.26 |
| Shear Modulus, GPa | 76 | |
| 34 |
| Shear Strength, MPa | 410 to 1410 | |
| 240 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 2470 | |
| 210 to 370 |
| Tensile Strength: Yield (Proof), MPa | 450 to 2290 | |
| 210 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 810 | |
| 100 |
| Melting Completion (Liquidus), °C | 1460 | |
| 400 |
| Melting Onset (Solidus), °C | 1420 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 440 |
| Thermal Expansion, µm/m-K | 11 | |
| 23 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 18 | |
| 11 |
| Density, g/cm3 | 7.9 | |
| 6.3 |
| Embodied Carbon, kg CO2/kg material | 4.1 | |
| 3.3 |
| Embodied Energy, MJ/kg | 55 | |
| 62 |
| Embodied Water, L/kg | 140 | |
| 420 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 48 to 130 | |
| 2.8 to 28 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 510 to 4780 | |
| 260 to 490 |
| Stiffness to Weight: Axial, points | 14 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 24 to 86 | |
| 9.3 to 17 |
| Strength to Weight: Bending, points | 22 to 51 | |
| 12 to 18 |
| Thermal Shock Resistance, points | 23 to 84 | |
| 7.6 to 13 |
Alloy Composition
| Aluminum (Al), % | 0.15 to 0.5 | |
| 8.0 to 8.8 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 11 to 13 | |
| 0 |
| Copper (Cu), % | 1.5 to 3.5 | |
| 0.8 to 1.3 |
| Iron (Fe), % | 65 to 76 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.015 to 0.030 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 3.0 to 5.0 | |
| 0 |
| Nickel (Ni), % | 8.0 to 10 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 |
| Silicon (Si), % | 0 to 0.7 | |
| 0 to 0.045 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Titanium (Ti), % | 0.5 to 1.2 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 89.7 to 91.2 |