S82013 Stainless Steel vs. EN 1.3576 Steel

Both S82013 stainless steel and EN 1.3576 steel are iron alloys. They have 76% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is S82013 stainless steel and the bottom bar is EN 1.3576 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
150 to 220
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 710
490 to 1420

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 970
420
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
46
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 11
3.4
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.4
1.7
Embodied Energy, MJ/kg 34
22
Embodied Water, L/kg 140
53

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26
17 to 50
Strength to Weight: Bending, points 23
17 to 36
Thermal Diffusivity, mm2/s 4.0
12
Thermal Shock Resistance, points 20
14 to 42

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.060
0.17 to 0.23
Chromium (Cr), % 19.5 to 22
0.35 to 0.65
Copper (Cu), % 0.2 to 1.2
0 to 0.3
Iron (Fe), % 70.5 to 77.1
95.5 to 97.5
Manganese (Mn), % 2.5 to 3.5
0.4 to 0.7
Molybdenum (Mo), % 0
0.2 to 0.3
Nickel (Ni), % 0.5 to 1.5
1.6 to 2.0
Nitrogen (N), % 0.2 to 0.3
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 0.9
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030