S82013 Stainless Steel vs. C83300 Brass

S82013 stainless steel belongs to the iron alloys classification, while C83300 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is S82013 stainless steel and the bottom bar is C83300 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 260
35
Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
35
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 78
42
Tensile Strength: Ultimate (UTS), MPa 710
220
Tensile Strength: Yield (Proof), MPa 500
69

Thermal Properties

Latent Heat of Fusion, J/g 290
200
Maximum Temperature: Mechanical, °C 970
180
Melting Completion (Liquidus), °C 1420
1060
Melting Onset (Solidus), °C 1380
1030
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 15
160
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
32
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
33

Otherwise Unclassified Properties

Base Metal Price, % relative 11
30
Density, g/cm3 7.7
8.8
Embodied Carbon, kg CO2/kg material 2.4
2.7
Embodied Energy, MJ/kg 34
44
Embodied Water, L/kg 140
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
60
Resilience: Unit (Modulus of Resilience), kJ/m3 640
21
Stiffness to Weight: Axial, points 14
7.0
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 26
6.9
Strength to Weight: Bending, points 23
9.2
Thermal Diffusivity, mm2/s 4.0
48
Thermal Shock Resistance, points 20
7.9

Alloy Composition

Carbon (C), % 0 to 0.060
0
Chromium (Cr), % 19.5 to 22
0
Copper (Cu), % 0.2 to 1.2
92 to 94
Iron (Fe), % 70.5 to 77.1
0
Lead (Pb), % 0
1.0 to 2.0
Manganese (Mn), % 2.5 to 3.5
0
Nickel (Ni), % 0.5 to 1.5
0
Nitrogen (N), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 0.9
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
1.0 to 2.0
Zinc (Zn), % 0
2.0 to 6.0
Residuals, % 0
0 to 0.7