ZK60A Magnesium vs. 3104 Aluminum
ZK60A magnesium belongs to the magnesium alloys classification, while 3104 aluminum belongs to the aluminum alloys.
For each property being compared, the top bar is ZK60A magnesium and the bottom bar is 3104 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 46 | |
| 70 |
| Elongation at Break, % | 4.5 to 9.9 | |
| 1.1 to 20 |
| Fatigue Strength, MPa | 150 to 180 | |
| 74 to 130 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 18 | |
| 26 |
| Shear Strength, MPa | 170 to 190 | |
| 110 to 180 |
| Tensile Strength: Ultimate (UTS), MPa | 320 to 330 | |
| 170 to 310 |
| Tensile Strength: Yield (Proof), MPa | 230 to 250 | |
| 68 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 180 |
| Melting Completion (Liquidus), °C | 600 | |
| 650 |
| Melting Onset (Solidus), °C | 550 | |
| 600 |
| Specific Heat Capacity, J/kg-K | 960 | |
| 900 |
| Thermal Conductivity, W/m-K | 120 | |
| 160 |
| Thermal Expansion, µm/m-K | 26 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 29 to 30 | |
| 41 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 130 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 13 | |
| 9.5 |
| Density, g/cm3 | 1.9 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 8.4 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 940 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 29 | |
| 1.6 to 60 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 570 to 690 | |
| 34 to 540 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 63 | |
| 50 |
| Strength to Weight: Axial, points | 47 to 49 | |
| 17 to 31 |
| Strength to Weight: Bending, points | 55 to 56 | |
| 25 to 37 |
| Thermal Diffusivity, mm2/s | 66 | |
| 64 |
| Thermal Shock Resistance, points | 19 to 20 | |
| 7.6 to 13 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 95.1 to 98.4 |
| Copper (Cu), % | 0 | |
| 0.050 to 0.25 |
| Gallium (Ga), % | 0 | |
| 0 to 0.050 |
| Iron (Fe), % | 0 | |
| 0 to 0.8 |
| Magnesium (Mg), % | 92.5 to 94.8 | |
| 0.8 to 1.3 |
| Manganese (Mn), % | 0 | |
| 0.8 to 1.4 |
| Silicon (Si), % | 0 | |
| 0 to 0.6 |
| Titanium (Ti), % | 0 | |
| 0 to 0.1 |
| Vanadium (V), % | 0 | |
| 0 to 0.050 |
| Zinc (Zn), % | 4.8 to 6.2 | |
| 0 to 0.25 |
| Zirconium (Zr), % | 0.45 to 1.0 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |