3004-H22 Aluminum
3004-H22 aluminum is 3004 aluminum in the H22 temper. To achieve this temper, the metal is strain hardened, and then partially annealed, to a strength that is roughly a quarter of the way between annealed (O) and full-hard (H28).
The graph bars on the material properties cards below compare 3004-H22 aluminum to: 3000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Brinell Hardness
58
Elastic (Young's, Tensile) Modulus
70 GPa 10 x 106 psi
Elongation at Break
4.3 %
Fatigue Strength
120 MPa 17 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Shear Strength
120 MPa 18 x 103 psi
Tensile Strength: Ultimate (UTS)
210 MPa 31 x 103 psi
Tensile Strength: Yield (Proof)
160 MPa 24 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
180 °C 360 °F
Melting Completion (Liquidus)
650 °C 1210 °F
Melting Onset (Solidus)
630 °C 1170 °F
Specific Heat Capacity
900 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
160 W/m-K 94 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
42 % IACS
Electrical Conductivity: Equal Weight (Specific)
140 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Calomel Potential
-750 mV
Density
2.8 g/cm3 170 lb/ft3
Embodied Carbon
8.3 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1180 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
8.4 MJ/m3
Resilience: Unit (Modulus of Resilience)
190 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
21 points
Strength to Weight: Bending
29 points
Thermal Diffusivity
65 mm2/s
Thermal Shock Resistance
9.2 points
Alloy Composition
| Al | 95.6 to 98.2 | |
| Mn | 1.0 to 1.5 | |
| Mg | 0.8 to 1.3 | |
| Fe | 0 to 0.7 | |
| Si | 0 to 0.3 | |
| Zn | 0 to 0.25 | |
| Cu | 0 to 0.25 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B547: Standard Specification for Aluminum and Aluminum-Alloy Formed and Arc-Welded Round Tube
Environmental Degradation of Advanced and Traditional Engineering Materials, Lloyd H. Hihara et al., 2014.
ASTM B209: Standard Specification for Aluminum and Aluminum-Alloy Sheet and Plate
EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
Aluminum Standards and Data, Aluminum Association Inc., 2013
ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties
EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993