3203-H14 Aluminum
3203-H14 aluminum is 3203 aluminum in the H14 temper. To achieve this temper, the metal is strain hardened to a strength that is roughly halfway between annealed (O) and full-hard (H18). The graph bars on the material properties cards below compare 3203-H14 aluminum to: 3000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
70 GPa 10 x 106 psi
Elongation at Break
9.1 %
Fatigue Strength
68 MPa 9.9 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Shear Strength
92 MPa 13 x 103 psi
Tensile Strength: Ultimate (UTS)
160 MPa 23 x 103 psi
Tensile Strength: Yield (Proof)
130 MPa 19 x 103 psi
Thermal Properties
Latent Heat of Fusion
400 J/g
Maximum Temperature: Mechanical
180 °C 360 °F
Melting Completion (Liquidus)
650 °C 1200 °F
Melting Onset (Solidus)
620 °C 1160 °F
Specific Heat Capacity
900 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
170 W/m-K 100 BTU/h-ft-°F
Thermal Expansion
23 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
43 % IACS
Electrical Conductivity: Equal Weight (Specific)
140 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.0 % relative
Density
2.8 g/cm3 170 lb/ft3
Embodied Carbon
8.1 kg CO2/kg material
Embodied Energy
150 MJ/kg 66 x 103 BTU/lb
Embodied Water
1180 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
13 MJ/m3
Resilience: Unit (Modulus of Resilience)
120 kJ/m3
Stiffness to Weight: Axial
14 points
Stiffness to Weight: Bending
50 points
Strength to Weight: Axial
16 points
Strength to Weight: Bending
23 points
Thermal Diffusivity
70 mm2/s
Thermal Shock Resistance
6.8 points
Alloy Composition
| Al | 96.9 to 99 | |
| Mn | 1.0 to 1.5 | |
| Fe | 0 to 0.7 | |
| Si | 0 to 0.6 | |
| Zn | 0 to 0.1 | |
| Cu | 0 to 0.050 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
Handbook of Aluminum Bonding Technology and Data, J. D. Minford, 1993
Aluminum: Properties and Physical Metallurgy, John E. Hatch (editor), 1984
ISO 6361-2: Wrought aluminium and aluminium alloys - Sheets, strips and plates - Part 2: Mechanical properties
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993