707.0-F Cast Aluminum
707.0-F aluminum is 707.0 aluminum in the as-fabricated (no temper or treatment) condition. It has the lowest strength compared to the other variants of 707.0 aluminum. The graph bars on the material properties cards below compare 707.0-F aluminum to: ANSI/AA cast aluminums (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
70 GPa 10 x 106 psi
Elongation at Break
1.7 %
Fatigue Strength
140 MPa 20 x 103 psi
Poisson's Ratio
0.33
Shear Modulus
26 GPa 3.8 x 106 psi
Tensile Strength: Ultimate (UTS)
270 MPa 40 x 103 psi
Tensile Strength: Yield (Proof)
200 MPa 29 x 103 psi
Thermal Properties
Latent Heat of Fusion
380 J/g
Maximum Temperature: Mechanical
180 °C 360 °F
Melting Completion (Liquidus)
630 °C 1170 °F
Melting Onset (Solidus)
600 °C 1110 °F
Solidification (Pattern Maker's) Shrinkage
1.6 %
Specific Heat Capacity
880 J/kg-K 0.21 BTU/lb-°F
Thermal Conductivity
150 W/m-K 85 BTU/h-ft-°F
Thermal Expansion
24 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
37 % IACS
Electrical Conductivity: Equal Weight (Specific)
110 % IACS
Otherwise Unclassified Properties
Base Metal Price
9.5 % relative
Density
2.9 g/cm3 180 lb/ft3
Embodied Carbon
8.3 kg CO2/kg material
Embodied Energy
150 MJ/kg 64 x 103 BTU/lb
Embodied Water
1140 L/kg 140 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
4.3 MJ/m3
Resilience: Unit (Modulus of Resilience)
290 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
47 points
Strength to Weight: Axial
26 points
Strength to Weight: Bending
32 points
Thermal Diffusivity
58 mm2/s
Thermal Shock Resistance
12 points
Alloy Composition
| Al | 90.5 to 93.6 | |
| Zn | 4.0 to 4.5 | |
| Mg | 1.8 to 2.4 | |
| Mn | 0.4 to 0.6 | |
| Fe | 0 to 0.8 | |
| Cr | 0.2 to 0.4 | |
| Ti | 0 to 0.25 | |
| Si | 0 to 0.2 | |
| Cu | 0 to 0.2 | |
| res. | 0 to 0.15 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B108: Standard Specification for Aluminum-Alloy Permanent Mold Castings
ASTM B26: Standard Specification for Aluminum-Alloy Sand Castings
Properties and Selection: Nonferrous Alloys and Special-Purpose Materials, ASM Handbook vol. 2, ASM International, 1993
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015