Stress Relieved Grade 364 Molybdenum
Stress relieved 364 molybdenum is grade 364 molybdenum in the stress relieved condition. The graph bars on the material properties cards below compare stress relieved 364 molybdenum to: molybdenum alloys (top), all alloys in the same category (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
310 GPa 45 x 106 psi
Elongation at Break
6.2 %
Poisson's Ratio
0.31
Shear Modulus
120 GPa 17 x 106 psi
Tensile Strength: Ultimate (UTS)
720 MPa 100 x 103 psi
Tensile Strength: Yield (Proof)
620 MPa 90 x 103 psi
Thermal Properties
Latent Heat of Fusion
370 J/g
Melting Completion (Liquidus)
2280 °C 4130 °F
Specific Heat Capacity
250 J/kg-K 0.060 BTU/lb-°F
Thermal Expansion
7.0 µm/m-K
Otherwise Unclassified Properties
Density
10 g/cm3 640 lb/ft3
Embodied Carbon
28 kg CO2/kg material
Embodied Energy
330 MJ/kg 140 x 103 BTU/lb
Embodied Water
360 L/kg 43 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
43 MJ/m3
Resilience: Unit (Modulus of Resilience)
630 kJ/m3
Stiffness to Weight: Axial
17 points
Stiffness to Weight: Bending
22 points
Strength to Weight: Axial
20 points
Strength to Weight: Bending
17 points
Thermal Shock Resistance
24 points
Alloy Composition
| Mo | 99.2 to 99.5 | |
| Ti | 0.4 to 0.55 | |
| Zr | 0.060 to 0.12 | |
| C | 0.010 to 0.040 | |
| O | 0 to 0.030 | |
| Fe | 0 to 0.010 | |
| Si | 0 to 0.0050 | |
| Ni | 0 to 0.0050 | |
| N | 0 to 0.0020 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Further Reading
ASTM B386: Standard Specification for Molybdenum and Molybdenum Alloy Plate, Sheet, Strip, and Foil
ASTM B387: Standard Specification for Molybdenum and Molybdenum Alloy Bar, Rod, and Wire
Sintering of Advanced Materials: Fundamentals and Processes, Zhigang Zak Fang (editor), 2010