296.0-T6 Aluminum vs. 7010-T6 Aluminum
Both 296.0-T6 aluminum and 7010-T6 aluminum are aluminum alloys. Both are furnished in the T6 temper. They have a moderately high 92% of their average alloy composition in common.
For each property being compared, the top bar is 296.0-T6 aluminum and the bottom bar is 7010-T6 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 90 | |
| 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 72 | |
| 70 |
| Elongation at Break, % | 3.2 | |
| 4.0 |
| Fatigue Strength, MPa | 70 | |
| 180 |
| Poisson's Ratio | 0.33 | |
| 0.32 |
| Shear Modulus, GPa | 27 | |
| 26 |
| Shear Strength, MPa | 220 | |
| 340 |
| Tensile Strength: Ultimate (UTS), MPa | 270 | |
| 590 |
| Tensile Strength: Yield (Proof), MPa | 180 | |
| 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 420 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 200 |
| Melting Completion (Liquidus), °C | 630 | |
| 630 |
| Melting Onset (Solidus), °C | 540 | |
| 480 |
| Specific Heat Capacity, J/kg-K | 870 | |
| 860 |
| Thermal Conductivity, W/m-K | 130 | |
| 150 |
| Thermal Expansion, µm/m-K | 22 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 33 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 99 | |
| 120 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 11 | |
| 10 |
| Density, g/cm3 | 3.0 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 7.8 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1110 | |
| 1120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 7.6 | |
| 23 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 | |
| 2050 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 46 | |
| 45 |
| Strength to Weight: Axial, points | 25 | |
| 54 |
| Strength to Weight: Bending, points | 31 | |
| 52 |
| Thermal Diffusivity, mm2/s | 51 | |
| 58 |
| Thermal Shock Resistance, points | 12 | |
| 26 |
Alloy Composition
| Aluminum (Al), % | 89 to 94 | |
| 87.9 to 90.6 |
| Chromium (Cr), % | 0 | |
| 0 to 0.050 |
| Copper (Cu), % | 4.0 to 5.0 | |
| 1.5 to 2.0 |
| Iron (Fe), % | 0 to 1.2 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 0 to 0.050 | |
| 2.1 to 2.6 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 to 0.35 | |
| 0 to 0.050 |
| Silicon (Si), % | 2.0 to 3.0 | |
| 0 to 0.12 |
| Titanium (Ti), % | 0 to 0.25 | |
| 0 to 0.060 |
| Zinc (Zn), % | 0 to 0.5 | |
| 5.7 to 6.7 |
| Zirconium (Zr), % | 0 | |
| 0.1 to 0.16 |
| Residuals, % | 0 | |
| 0 to 0.15 |