3103 Aluminum vs. AM60A Magnesium
3103 aluminum belongs to the aluminum alloys classification, while AM60A magnesium belongs to the magnesium alloys.
For each property being compared, the top bar is 3103 aluminum and the bottom bar is AM60A magnesium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 27 to 62 | |
| 62 |
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 45 |
| Elongation at Break, % | 1.1 to 28 | |
| 8.8 |
| Fatigue Strength, MPa | 38 to 83 | |
| 70 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 26 | |
| 18 |
| Shear Strength, MPa | 68 to 130 | |
| 130 |
| Tensile Strength: Ultimate (UTS), MPa | 100 to 220 | |
| 230 |
| Tensile Strength: Yield (Proof), MPa | 39 to 200 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 350 |
| Maximum Temperature: Mechanical, °C | 190 | |
| 120 |
| Melting Completion (Liquidus), °C | 660 | |
| 620 |
| Melting Onset (Solidus), °C | 640 | |
| 550 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 1000 |
| Thermal Conductivity, W/m-K | 160 | |
| 62 |
| Thermal Expansion, µm/m-K | 23 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 42 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 140 | |
| 69 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 12 |
| Density, g/cm3 | 2.8 | |
| 1.7 |
| Embodied Carbon, kg CO2/kg material | 8.2 | |
| 23 |
| Embodied Energy, MJ/kg | 150 | |
| 160 |
| Embodied Water, L/kg | 1180 | |
| 990 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 2.4 to 24 | |
| 17 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 11 to 280 | |
| 190 |
| Stiffness to Weight: Axial, points | 14 | |
| 15 |
| Stiffness to Weight: Bending, points | 50 | |
| 71 |
| Strength to Weight: Axial, points | 10 to 22 | |
| 37 |
| Strength to Weight: Bending, points | 18 to 30 | |
| 49 |
| Thermal Diffusivity, mm2/s | 64 | |
| 37 |
| Thermal Shock Resistance, points | 4.6 to 9.9 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 96.3 to 99.1 | |
| 5.5 to 6.5 |
| Chromium (Cr), % | 0 to 0.1 | |
| 0 |
| Copper (Cu), % | 0 to 0.1 | |
| 0 to 0.35 |
| Iron (Fe), % | 0 to 0.7 | |
| 0 |
| Magnesium (Mg), % | 0 to 0.3 | |
| 91.8 to 94.4 |
| Manganese (Mn), % | 0.9 to 1.5 | |
| 0.13 to 0.6 |
| Nickel (Ni), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.5 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 0 to 0.22 |
| Zirconium (Zr), % | 0 to 0.1 | |
| 0 |
| Residuals, % | 0 to 0.15 | |
| 0 |