3104 Aluminum vs. 6463 Aluminum
Both 3104 aluminum and 6463 aluminum are aluminum alloys. They have a very high 98% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is 3104 aluminum and the bottom bar is 6463 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 70 | |
| 68 |
| Elongation at Break, % | 1.1 to 20 | |
| 9.0 to 17 |
| Fatigue Strength, MPa | 74 to 130 | |
| 45 to 76 |
| Poisson's Ratio | 0.33 | |
| 0.33 |
| Shear Modulus, GPa | 26 | |
| 26 |
| Shear Strength, MPa | 110 to 180 | |
| 86 to 150 |
| Tensile Strength: Ultimate (UTS), MPa | 170 to 310 | |
| 140 to 230 |
| Tensile Strength: Yield (Proof), MPa | 68 to 270 | |
| 82 to 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 400 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 160 |
| Melting Completion (Liquidus), °C | 650 | |
| 660 |
| Melting Onset (Solidus), °C | 600 | |
| 620 |
| Specific Heat Capacity, J/kg-K | 900 | |
| 900 |
| Thermal Conductivity, W/m-K | 160 | |
| 190 to 210 |
| Thermal Expansion, µm/m-K | 23 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 41 | |
| 50 to 55 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 170 to 180 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 9.5 | |
| 9.5 |
| Density, g/cm3 | 2.8 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 8.4 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 1180 | |
| 1190 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 1.6 to 60 | |
| 17 to 25 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 34 to 540 | |
| 50 to 300 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 50 | |
| 50 |
| Strength to Weight: Axial, points | 17 to 31 | |
| 14 to 24 |
| Strength to Weight: Bending, points | 25 to 37 | |
| 22 to 31 |
| Thermal Diffusivity, mm2/s | 64 | |
| 79 to 86 |
| Thermal Shock Resistance, points | 7.6 to 13 | |
| 6.3 to 10 |
Alloy Composition
| Aluminum (Al), % | 95.1 to 98.4 | |
| 97.9 to 99.4 |
| Copper (Cu), % | 0.050 to 0.25 | |
| 0 to 0.2 |
| Gallium (Ga), % | 0 to 0.050 | |
| 0 |
| Iron (Fe), % | 0 to 0.8 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 0.8 to 1.3 | |
| 0.45 to 0.9 |
| Manganese (Mn), % | 0.8 to 1.4 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 to 0.6 | |
| 0.2 to 0.6 |
| Titanium (Ti), % | 0 to 0.1 | |
| 0 |
| Vanadium (V), % | 0 to 0.050 | |
| 0 |
| Zinc (Zn), % | 0 to 0.25 | |
| 0 to 0.050 |
| Residuals, % | 0 | |
| 0 to 0.15 |