AWS ERNi-1 vs. Grade 364 Molybdenum
AWS ERNi-1 belongs to the nickel alloys classification, while grade 364 molybdenum belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS ERNi-1 and the bottom bar is grade 364 molybdenum.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 180 | |
310 |
Elongation at Break, % | 22 | |
6.2 to 11 |
Poisson's Ratio | 0.31 | |
0.31 |
Shear Modulus, GPa | 69 | |
120 |
Tensile Strength: Ultimate (UTS), MPa | 470 | |
580 to 720 |
Thermal Properties
Latent Heat of Fusion, J/g | 300 | |
370 |
Specific Heat Capacity, J/kg-K | 450 | |
250 |
Thermal Expansion, µm/m-K | 11 | |
7.0 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.7 | |
10 |
Embodied Carbon, kg CO2/kg material | 11 | |
28 |
Embodied Energy, MJ/kg | 150 | |
330 |
Embodied Water, L/kg | 230 | |
360 |
Common Calculations
Stiffness to Weight: Axial, points | 12 | |
17 |
Stiffness to Weight: Bending, points | 22 | |
22 |
Strength to Weight: Axial, points | 15 | |
16 to 20 |
Strength to Weight: Bending, points | 15 | |
15 to 17 |
Thermal Shock Resistance, points | 17 | |
19 to 24 |
Alloy Composition
Aluminum (Al), % | 0 to 1.5 | |
0 |
Carbon (C), % | 0 to 0.15 | |
0.010 to 0.040 |
Copper (Cu), % | 0 to 0.25 | |
0 |
Iron (Fe), % | 0 to 1.0 | |
0 to 0.010 |
Manganese (Mn), % | 0 to 1.0 | |
0 |
Molybdenum (Mo), % | 0 | |
99.2 to 99.5 |
Nickel (Ni), % | 93 to 98 | |
0 to 0.0050 |
Nitrogen (N), % | 0 | |
0 to 0.0020 |
Oxygen (O), % | 0 | |
0 to 0.030 |
Phosphorus (P), % | 0 to 0.030 | |
0 |
Silicon (Si), % | 0 to 0.75 | |
0 to 0.0050 |
Sulfur (S), % | 0 to 0.015 | |
0 |
Titanium (Ti), % | 2.0 to 3.5 | |
0.4 to 0.55 |
Zirconium (Zr), % | 0 | |
0.060 to 0.12 |
Residuals, % | 0 to 0.5 | |
0 |