EN 1.4311 Stainless Steel vs. ASTM A356 Grade 10

Both EN 1.4311 stainless steel and ASTM A356 grade 10 are iron alloys. They have 73% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4311 stainless steel and the bottom bar is ASTM A356 grade 10.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
200
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 43
23
Fatigue Strength, MPa 270
300
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
74
Tensile Strength: Ultimate (UTS), MPa 650
670
Tensile Strength: Yield (Proof), MPa 310
430

Thermal Properties

Latent Heat of Fusion, J/g 290
260
Maximum Temperature: Mechanical, °C 950
460
Melting Completion (Liquidus), °C 1420
1470
Melting Onset (Solidus), °C 1380
1430
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
39
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 16
3.9
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.1
1.8
Embodied Energy, MJ/kg 43
23
Embodied Water, L/kg 140
59

Common Calculations

PREN (Pitting Resistance) 21
5.9
Resilience: Ultimate (Unit Rupture Work), MJ/m3 230
130
Resilience: Unit (Modulus of Resilience), kJ/m3 240
480
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 23
24
Strength to Weight: Bending, points 21
22
Thermal Diffusivity, mm2/s 4.0
11
Thermal Shock Resistance, points 15
19

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.2
Chromium (Cr), % 17.5 to 19.5
2.0 to 2.8
Iron (Fe), % 65.7 to 73.9
94.4 to 96.6
Manganese (Mn), % 0 to 2.0
0.5 to 0.8
Molybdenum (Mo), % 0
0.9 to 1.2
Nickel (Ni), % 8.5 to 11.5
0
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.030