EN 1.4563 Stainless Steel vs. EN 1.0345 Steel

Both EN 1.4563 stainless steel and EN 1.0345 steel are iron alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4563 stainless steel and the bottom bar is EN 1.0345 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200
120
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
27
Fatigue Strength, MPa 210
170
Impact Strength: V-Notched Charpy, J 91
44
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 420
270
Tensile Strength: Ultimate (UTS), MPa 620
420
Tensile Strength: Yield (Proof), MPa 250
230

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 12
49
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 36
2.1
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.3
1.5
Embodied Energy, MJ/kg 87
19
Embodied Water, L/kg 240
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
96
Resilience: Unit (Modulus of Resilience), kJ/m3 150
140
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21
15
Strength to Weight: Bending, points 20
16
Thermal Diffusivity, mm2/s 3.2
13
Thermal Shock Resistance, points 13
13

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.024
Carbon (C), % 0 to 0.020
0 to 0.16
Chromium (Cr), % 26 to 28
0 to 0.3
Copper (Cu), % 0.7 to 1.5
0 to 0.3
Iron (Fe), % 31.6 to 40.3
97.2 to 99.38
Manganese (Mn), % 0 to 2.0
0.6 to 1.2
Molybdenum (Mo), % 3.0 to 4.0
0 to 0.080
Nickel (Ni), % 30 to 32
0 to 0.3
Niobium (Nb), % 0
0 to 0.020
Nitrogen (N), % 0 to 0.1
0 to 0.012
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.7
0 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.010
Titanium (Ti), % 0
0 to 0.030
Vanadium (V), % 0
0 to 0.020