EN 1.4563 Stainless Steel vs. EN 1.4011 Stainless Steel

Both EN 1.4563 stainless steel and EN 1.4011 stainless steel are iron alloys. They have 50% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4563 stainless steel and the bottom bar is EN 1.4011 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
17
Fatigue Strength, MPa 210
310
Impact Strength: V-Notched Charpy, J 91
23
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 620
700
Tensile Strength: Yield (Proof), MPa 250
510

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Corrosion, °C 460
390
Maximum Temperature: Mechanical, °C 1100
750
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 12
25
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 36
7.0
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.3
2.0
Embodied Energy, MJ/kg 87
28
Embodied Water, L/kg 240
100

Common Calculations

PREN (Pitting Resistance) 39
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 200
110
Resilience: Unit (Modulus of Resilience), kJ/m3 150
660
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 21
25
Strength to Weight: Bending, points 20
23
Thermal Diffusivity, mm2/s 3.2
6.7
Thermal Shock Resistance, points 13
24

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.15
Chromium (Cr), % 26 to 28
11.5 to 13.5
Copper (Cu), % 0.7 to 1.5
0
Iron (Fe), % 31.6 to 40.3
82.8 to 88.5
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 3.0 to 4.0
0 to 0.5
Nickel (Ni), % 30 to 32
0 to 1.0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.7
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.025