SAE-AISI 1144 Steel vs. Monel 400

SAE-AISI 1144 steel belongs to the iron alloys classification, while Monel 400 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is SAE-AISI 1144 steel and the bottom bar is Monel 400.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
160
Elongation at Break, % 11 to 17
20 to 40
Fatigue Strength, MPa 280 to 430
230 to 290
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 72
62
Shear Strength, MPa 460 to 510
370 to 490
Tensile Strength: Ultimate (UTS), MPa 750 to 840
540 to 780
Tensile Strength: Yield (Proof), MPa 420 to 690
210 to 590

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
1000
Melting Completion (Liquidus), °C 1450
1350
Melting Onset (Solidus), °C 1410
1300
Specific Heat Capacity, J/kg-K 470
430
Thermal Conductivity, W/m-K 51
23
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
3.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
50
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.4
7.9
Embodied Energy, MJ/kg 19
110
Embodied Water, L/kg 47
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91 to 110
140 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 480 to 1290
140 to 1080
Stiffness to Weight: Axial, points 13
10
Stiffness to Weight: Bending, points 24
21
Strength to Weight: Axial, points 27 to 30
17 to 25
Strength to Weight: Bending, points 23 to 25
17 to 21
Thermal Diffusivity, mm2/s 14
6.1
Thermal Shock Resistance, points 22 to 24
17 to 25

Alloy Composition

Carbon (C), % 0.4 to 0.48
0 to 0.3
Copper (Cu), % 0
28 to 34
Iron (Fe), % 97.5 to 98
0 to 2.5
Manganese (Mn), % 1.4 to 1.7
0 to 2.0
Nickel (Ni), % 0
63 to 72
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0
0 to 0.5
Sulfur (S), % 0.24 to 0.33
0 to 0.024

Comparable Variants