N08332 Stainless Steel vs. C22000 Bronze
N08332 stainless steel belongs to the iron alloys classification, while C22000 bronze belongs to the copper alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is N08332 stainless steel and the bottom bar is C22000 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
110 |
Elongation at Break, % | 34 | |
1.9 to 45 |
Poisson's Ratio | 0.28 | |
0.33 |
Rockwell B Hardness | 77 | |
42 to 81 |
Shear Modulus, GPa | 76 | |
42 |
Shear Strength, MPa | 350 | |
200 to 300 |
Tensile Strength: Ultimate (UTS), MPa | 520 | |
260 to 520 |
Tensile Strength: Yield (Proof), MPa | 210 | |
69 to 500 |
Thermal Properties
Latent Heat of Fusion, J/g | 310 | |
200 |
Maximum Temperature: Mechanical, °C | 1050 | |
180 |
Melting Completion (Liquidus), °C | 1390 | |
1040 |
Melting Onset (Solidus), °C | 1340 | |
1020 |
Specific Heat Capacity, J/kg-K | 480 | |
390 |
Thermal Conductivity, W/m-K | 12 | |
190 |
Thermal Expansion, µm/m-K | 16 | |
18 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 1.7 | |
44 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 1.9 | |
45 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 32 | |
29 |
Density, g/cm3 | 8.0 | |
8.7 |
Embodied Carbon, kg CO2/kg material | 5.4 | |
2.6 |
Embodied Energy, MJ/kg | 77 | |
42 |
Embodied Water, L/kg | 190 | |
310 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 | |
3.7 to 230 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 | |
21 to 1110 |
Stiffness to Weight: Axial, points | 14 | |
7.2 |
Stiffness to Weight: Bending, points | 24 | |
18 |
Strength to Weight: Axial, points | 18 | |
8.1 to 17 |
Strength to Weight: Bending, points | 18 | |
10 to 17 |
Thermal Diffusivity, mm2/s | 3.1 | |
56 |
Thermal Shock Resistance, points | 12 | |
8.8 to 18 |
Alloy Composition
Carbon (C), % | 0.050 to 0.1 | |
0 |
Chromium (Cr), % | 17 to 20 | |
0 |
Copper (Cu), % | 0 to 1.0 | |
89 to 91 |
Iron (Fe), % | 38.3 to 48.2 | |
0 to 0.050 |
Lead (Pb), % | 0 to 0.0050 | |
0 to 0.050 |
Manganese (Mn), % | 0 to 2.0 | |
0 |
Nickel (Ni), % | 34 to 37 | |
0 |
Phosphorus (P), % | 0 to 0.030 | |
0 |
Silicon (Si), % | 0.75 to 1.5 | |
0 |
Sulfur (S), % | 0 to 0.030 | |
0 |
Tin (Sn), % | 0 to 0.025 | |
0 |
Zinc (Zn), % | 0 | |
8.7 to 11 |
Residuals, % | 0 | |
0 to 0.2 |