S30452 Stainless Steel vs. S15700 Stainless Steel

Both S30452 stainless steel and S15700 stainless steel are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is S30452 stainless steel and the bottom bar is S15700 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
200 to 460
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
1.1 to 29
Fatigue Strength, MPa 250
370 to 770
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Shear Strength, MPa 440
770 to 1070
Tensile Strength: Ultimate (UTS), MPa 660
1180 to 1890
Tensile Strength: Yield (Proof), MPa 310
500 to 1770

Thermal Properties

Latent Heat of Fusion, J/g 290
290
Maximum Temperature: Corrosion, °C 420
400
Maximum Temperature: Mechanical, °C 960
870
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
16
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.4
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.7
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 15
15
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.0
3.4
Embodied Energy, MJ/kg 43
47
Embodied Water, L/kg 150
140

Common Calculations

PREN (Pitting Resistance) 23
23
Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
17 to 270
Resilience: Unit (Modulus of Resilience), kJ/m3 250
640 to 4660
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
42 to 67
Strength to Weight: Bending, points 22
32 to 43
Thermal Diffusivity, mm2/s 4.2
4.2
Thermal Shock Resistance, points 15
39 to 63

Alloy Composition

Aluminum (Al), % 0
0.75 to 1.5
Carbon (C), % 0 to 0.080
0 to 0.090
Chromium (Cr), % 18 to 20
14 to 16
Iron (Fe), % 66.3 to 73.8
69.6 to 76.8
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
2.0 to 3.0
Nickel (Ni), % 8.0 to 10.5
6.5 to 7.7
Nitrogen (N), % 0.16 to 0.3
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030